ABS Resin 3100R
  • ABS Resin 3100R

ABS Resin 3100R

Production country: Taiwan

Cost in place: Moscow

Выберите город:

Цена по запросу

Min. order qty 17 t

Основные характеристики

  • Brand

    TAITALAC®

  • Grade

    Super high impact grade, High Rigidity grade

  • Processing method

    Extrusion, Injection Molding

  • Tensile Strength at Yield

    42 MPa

  • Tensile Strength at Break

    37 MPa

  • Elongation at Break

    30 %

  • Melt flow index

    8 g/10min

  • Rockwell Hardness

    100 R-scale

Similar goods

Описание:

ABS is the terpolymer of Acrylonitrile-Butadiene-Styrene. Each of the three components possesses certain functions. Acrylonitrile provides chemical resistance and hardness, Butadiene contributes toughness and impact strength; Styrene offers gloss and process-ability. Combining the above characteristics, ABS is now the most popular and economical Engineering Plastic.

TAITALAC®is the trade name of TTC’s ABS resin. Adopting the famous Japanese Toray Process, TAITALAC® is enjoying a reputation for excellent quality and recognized as one of the leading ABS / SAN resins in the world.

ABS Resin TAITALAC® 3100R description:

  • Extrusion/Injection
  • Super high impact strength and rigidity  

APPLICATION 

  • motorcycle parts,
  • helmets,
  • shoe heels
  • products for low temperature use,
  • Profile Extrusion
  • Automobile parts

General properties

  • Grade: Super high impact grade, High Rigidity grade
  • Processing method: Extrusion, Injection Molding
  • Application: Automobile/Motorcycle parts , Low temperature use, Helmets , Shoes and parts, Tool boxes, Luggage , Profile Extrusion

Thermal properties

  • Test Condition:: 220℃, 10kg load
  • Melt flow index: 8 g/10min
  • Heat Distortion Temperature : 87 °C
  • Vicat Softening Temperature : 103 °C

Mechanical properties

  • Test Condition: : 23℃, 1/8 inch, 5 mm/min
  • Tensile Strength at Yield: 42 MPa
  • Tensile Strength at Break : 37 MPa
  • Elongation at Break : 30 %
  • Flexural yield strength: 62 MPa
  • Flexural Modulus : 2200 MPa

Physical properties

  • Rockwell Hardness : 100 R-scale
  • Mold Shrinkage: 0.4 %
  • Water Absorption : 0.3 %
  • Izod Impact Strength: 47.01 kg-cm/cm
  • Test Condition : 23℃, 1/8" notched