PC Resin PC-110U
  • PC Resin PC-110U

PC Resin PC-110U

Production country: Taiwan

Основные характеристики

  • Brand

    WONDERLITE®

  • Grade

    Weathering grade

  • Processing method

    Injection Molding

  • Tensile Strength at Yield

    65 MPa

  • Elongation at Break

    120 %

  • Melt flow index

    10 g/10min

Similar goods

Описание:

Polycarbonate resin polymerized using the double hydroxy compounds of BPA (bisphenol-A) and the diphenylcarbonates of carbonate compounds with the transesterification (melting) method. Absolutely no phosgene and chlorinated solvents such as dichloromethane were used during the manufacturing process. Our polycarbonate resins are FDA and UL certified.

Polycarbonate Resin has excellent transparency, high heat resistance, ultra high impact resistance, dimensional stability, etc., making it suitable for a wide range of applications. All 3C products, electrical and electronic products, precision machinery, instrument products, automotive parts, sporting goods, recreational goods, sanitary hygiene products, CD/DVD related products, etc.

Characteristics:

  • For General Injection Molding

Applications

  • Outdoor application
  • Traffic sign

General properties

  • Grade: Weathering grade
  • Processing method: Injection Molding
  • Application: Outdoor application, Traffic signs

Thermal properties

  • Test Condition:: 300℃, 1.2kg load
  • Melt flow index: 10 g/10min
  • Heat Distortion Temperature : 127 °
  • Vicat Softening Temperature : 143 °

Mechanical properties

  • Test Condition: : 23℃, 1/8 inch, 5 mm/min
  • Tensile Strength at Yield: 65 MPa
  • Tensile Strength at Break : 75 MPa
  • Elongation at Break : 120 %
  • Flexural yield strength: 90 MPa
  • Flexural Modulus : 2400 MPa

Physical properties

  • Rockwell Hardness : 77 R-scale
  • Mold Shrinkage: 0.6 %
  • Izod Impact Strength: 87 kg-cm/cm
  • Test Condition : 23℃, 1/8" notched kg-cm/cm