SAN-resin SAN 1600H
  • SAN-resin SAN 1600H

SAN-resin SAN 1600H

Production country: Taiwan

Cost in place: Moscow

Выберите город:

Цена по запросу

Min. order qty 17 t

Основные характеристики

  • Brand

    TAITALAC®

  • Grade

    High heat resistant grade, High chemical resistant

  • Processing method

    Injection Molding

  • Tensile Strength at Yield

    81 MPa

  • Tensile Strength at Break

    75 MPa

  • Melt flow index

    1.2 g/10min

Similar goods

Описание:

SAN is a copolymerization of styrene-acrylonitrile. Acrylonitrile monomer (AN) is added to styrene monomer (SM) to copolymerize SAN, also commonly known as the AS Resin. SAN not only retains the transparency of GPPS, it also has more chemical resistance and slightly increased surface hardness. Under natural conditions, it is a bright yellowish transparent object.

SAV Resin TAITALAC® SAN1600H description:

  • Injection
  • Compounding
  • Lighter

APPLICATION 

  • Blade of fan 
  • Batteries casings 
  • Toothbrush handles 
  • Any transparent molded products requiring high strength.
  • Lighters casings

General properties

  • Grade: High heat resistant grade, High chemical resistant
  • Processing method: Injection Molding
  • Application: General chemical resistance products, Lighters casings, Toothbrush handles, Fan blades, Vegetable boxes in refrigerators, High strengt transparent products

Thermal properties

  • Test Condition:: 200℃, 5kg load MPa
  • Melt flow index: 1.2 g/10min
  • Heat Distortion Temperature : 95 °
  • Vicat Softening Temperature : 108 °

Mechanical properties

  • Test Condition: : 23℃, 1/8 inch, 5 mm/min
  • Tensile Strength at Yield: 81 MPa
  • Tensile Strength at Break : 75 MPa
  • Elongation at Break : 8 %
  • Flexural yield strength: 120 MPa
  • Flexural Modulus : 3600 MPa

Physical properties

  • Rockwell Hardness : 85 R-scale
  • Mold Shrinkage: 0.5 %
  • Izod Impact Strength: 2.5 kg-cm/cm
  • Test Condition : 23℃, 1/8" notched