ABS Resin 3000P
  • ABS Resin 3000P

ABS Resin 3000P

Production country: Taiwan

Основные характеристики

  • Brand

    TAITALAC®

  • Grade

    Super high impact grade, High Rigidity grade

  • Processing method

    Extrusion, Injection Molding

  • Tensile Strength at Yield

    36 MPa

  • Tensile Strength at Break

    33 MPa

  • Elongation at Break

    50 %

  • Melt flow index

    9 g/10min

  • Rockwell Hardness

    100 R-scale

Similar goods

Описание:

ABS is the terpolymer of Acrylonitrile-Butadiene-Styrene. Each of the three components possesses certain functions. Acrylonitrile provides chemical resistance and hardness, Butadiene contributes toughness and impact strength; Styrene offers gloss and process-ability. Combining the above characteristics, ABS is now the most popular and economical Engineering Plastic.

TAITALAC®is the trade name of TTC’s ABS resin. Adopting the famous Japanese Toray Process, TAITALAC® is enjoying a reputation for excellent quality and recognized as one of the leading ABS / SAN resins in the world.

ABS Resin TAITALAC® 3000P description:

  • Extrusion/Injection
  • Super high impact strength and rigidity  

APPLICATION 

  • Luggage 
  • tool boxes,
  • motorcycle parts,
  • helmets,
  • attache cases
  • shoe heels
  • products for low temperature use,
  • extruded pipe

General properties

  • Grade: Super high impact grade, High Rigidity grade
  • Processing method: Extrusion, Injection Molding
  • Application: Automobile/Motorcycle parts , Low temperature use, Helmets , Shoes and parts, Tool boxes, Luggage , Extruded pipes

Thermal properties

  • Test Condition:: 220℃, 10kg load
  • Melt flow index: 9 g/10min
  • Heat Distortion Temperature : 86 °C
  • Vicat Softening Temperature : 103 °C

Mechanical properties

  • Test Condition: : 23℃, 1/8 inch, 5 mm/min
  • Tensile Strength at Yield: 36 MPa
  • Tensile Strength at Break : 33 MPa
  • Elongation at Break : 50 %
  • Flexural yield strength: 58 MPa
  • Flexural Modulus : 2000 MPa

Physical properties

  • Rockwell Hardness : 100 R-scale
  • Mold Shrinkage: 0.4 %
  • Water Absorption : 0.3 %
  • Izod Impact Strength: 47 kg-cm/cm
  • Test Condition : 23℃, 1/8" notched