SAN-resin SAN 1300
  • SAN-resin SAN 1300

SAN-resin SAN 1300

Production country: Taiwan

Cost in place: Moscow

Выберите город:

Цена по запросу

Min. order qty 17 t

Основные характеристики

  • Brand

    TAITALAC®

  • Grade

    General purpose grade

  • Processing method

    Injection Molding

  • Tensile Strength at Yield

    70 MPa

  • Tensile Strength at Break

    69 MPa

  • Melt flow index

    50 g/10min

Similar goods

Описание:

SAN is a copolymerization of styrene-acrylonitrile. Acrylonitrile monomer (AN) is added to styrene monomer (SM) to copolymerize SAN, also commonly known as the AS Resin. SAN not only retains the transparency of GPPS, it also has more chemical resistance and slightly increased surface hardness. Under natural conditions, it is a bright yellowish transparent object.

SAV Resin TAITALAC® SAN1600H description:

  • Injection

APPLICATION 

  • Daily commodities 
  • Lamp covers 
  • Pen tube 
  • Cup with cover 
  • Cosmetic cases 
  • Family hardware transparent products 
  • Fruit and vegetable boxes in refrigerator

General properties

  • Grade: General purpose grade
  • Processing method: Injection Molding
  • Application: Food containers/cans, House-ware transparent products, Cosmetic boxes, Lamp covers, Daily commodities, Vegetable boxes in refrigerators, Pen tubes

Thermal properties

  • Test Condition:: 200℃, 5kg load MPa
  • Melt flow index: 50 g/10min
  • Heat Distortion Temperature : 90 °
  • Vicat Softening Temperature : 103 °

Mechanical properties

  • Test Condition: : 23℃, 1/8 inch, 5 mm/min
  • Tensile Strength at Yield: 70 MPa
  • Tensile Strength at Break : 69 MPa
  • Elongation at Break : 5 %
  • Flexural yield strength: 110 MPa
  • Flexural Modulus : 3400 MPa

Physical properties

  • Rockwell Hardness : 82 R-scale
  • Mold Shrinkage: 0.5 %
  • Izod Impact Strength: 1.8 kg-cm/cm
  • Test Condition : 23℃, 1/8" notched