SAN-resin PN-117C
  • SAN-resin PN-117C

SAN-resin PN-117C

Production country: Taiwan

Cost in place: Moscow

Выберите город:

Цена по запросу

Min. order qty 17 t

Основные характеристики

  • Brand

    KIBISAN®

  • Grade

    High flowability grade

  • Processing method

    Injection Molding

  • Tensile Strength at Yield

    67 MPa

  • Melt flow index

    58 g/10min

Similar goods

Описание:

SAN is a copolymerization of styrene-acrylonitrile. Acrylonitrile monomer (AN) is added to styrene monomer (SM) to copolymerize SAN, also commonly known as the AS Resin. SAN not only retains the transparency of GPPS, it also has more chemical resistance and slightly increased surface hardness. Under natural conditions, it is a bright yellowish transparent object.

Application:

Daily commodities / family hardware transparent products / cosmetic boxes

General properties

  • Grade: High flowability grade
  • Processing method: Injection Molding
  • Application: Daily commodities, Vegetable boxes in refrigerators

Thermal properties

  • Test Condition:: 220℃, 10kg load MPa
  • Melt flow index: 58 g/10min
  • Heat Distortion Temperature : 89 °
  • Vicat Softening Temperature : 104 °

Mechanical properties

  • Test Condition: : 23℃, 1/8 inch, 5 mm/min
  • Tensile Strength at Yield: 67 MPa
  • Tensile Strength at Break : 67 MPa
  • Elongation at Break : 6 %
  • Flexural yield strength: 89 MPa
  • Flexural Modulus : 2700 MPa

Physical properties

  • Mold Shrinkage: 0.5 %
  • Izod Impact Strength: 1.8 kg-cm/cm
  • Test Condition : 23℃, 1/8" notched